BAHUBALI Alloys have refractory Anchor 310H type shows astounding impervious to oxidation under gently cyclic conditions through to 2000°F attributes. Also, in light of its high chromium and medium nickel substance, 310H type has great impervious to protection and different types of hot erosion.
Refractory Anchor 310H type is generally utilized as a part of respectably carbonizing environments, for example, those experienced in petrochemical situations. The all the more extremely carbonizing climates of modern warmth treating heaters require RA-330® or RA-333®.
Table 1. Composition ranges for Stainless Steel 310H Refractory Anchors
Table 2. Mechanical properties of Stainless Steel 310H Refractory Anchors
|Grade||Tensile Strength (MPa) min||Yield Strength 0.2% Proof (MPa) min||Elongation (% in 50mm) min||Hardness|
|Rockwell B (HR B) max||Brinell (HB) max|
|310H also has a requirement for a grain size of ASTM No 7 or coarser.|
Table 3. Physical properties of Stainless Steel 310H Refractory Anchors
|Density (kg/m3)||Elastic Modulus (GPa)||Mean Coefficient of Thermal Expansion (m/m/0C)||Thermal Conductivity (W/m.K)||Specific Heat 0-1000C (J/kg.K)||Electrical Resistivity (n.m)|
|0-1000C||0-3150C||0-5380C||at 1000C||at 5000C|
Table 4. Grade specifications for Stainless Steel 310H Refractory Anchors
|Grade||UNS No||Old British||Euronorm||Swedish SS||Japanese JIS|
|These comparisons are approximate only. The list is intended as a comparison of functionally similar materials not as a schedule of contractual equivalents. If exact equivalents are needed original specifications must be consulted.|
Table 5. Standard specifications for Stainless Steel 310H Refractory Anchors
|Form||V shape, Y shape and crook anchors but as per clients drawings and requirements.|